离子束辅助沉积大口径光学薄膜

艾万君, 熊胜明

文章导航 > 红外与激光工程 > 2015 > 44(S1): 183-188

艾万君, 熊胜明. 离子束辅助沉积大口径光学薄膜[J]. 红外与激光工程, 2015, 44(S1): 183-188.

引用本文:

艾万君, 熊胜明. 离子束辅助沉积大口径光学薄膜[J]. 红外与激光工程, 2015, 44(S1): 183-188.

Ai Wanjun, Xiong Shengming. Large optical coatings fabricated by ion assisted technology[J]. Infrared and Laser Engineering, 2015, 44(S1): 183-188.

Citation:

Ai Wanjun, Xiong Shengming. Large optical coatings fabricated by ion assisted technology[J]. Infrared and Laser Engineering, 2015, 44(S1): 183-188.

离子束辅助沉积大口径光学薄膜

1.
中国科学院光电技术研究所,四川成都 610209

详细信息

作者简介:
艾万君(1985-),男,硕士生,主要从事光学薄膜的制备及其特性方面的研究。Email:awj422177370@163.com

中图分类号: O484.4

Large optical coatings fabricated by ion assisted technology

1.
Institute of Optics and Electronics,Chinese Academy of Sciences,Chengdu 610209,China

摘要: 利用国内最大箱式高真空镀膜设备ZZS3600,开展了双离子束辅助反应蒸发技术及光学薄膜厚度均匀性研究。借助MarkⅡ离子源辅助反应蒸发技术,对Ta2O5、SiO2常见的高、低折射率光学薄膜进行了制备与特性分析。结果表明:在蒸发源与沉积基底距离较大的镀膜环境下,具有低能、高束流密度离子源有利于薄膜结构的致密化,薄膜性能的改善。根据大口径光学元件尺寸,结合真空室空间几何配置,开展了行星及单轴转动方式下镀膜膜厚均匀性的研究。行星转动方式下,分析了直径140 cm行星盘工件膜厚均匀性,无修正挡板运行时膜厚不均匀性优于0.4%。单轴转动方式下,分析了200 cm光学元件膜厚均匀性,并通过设计修正挡板将膜厚不均匀性控制在0.6%以内。采用双离子束辅助反应蒸发技术有利于实现高性能大口径光学薄膜的制备。
- 离子辅助沉积 /
- 高真空镀膜设备 /
- 大口径光学薄膜 /
- 光学特性 /
- 膜厚均匀性
Abstract: Optical coatings were fabricated by ion assisted deposition technology based on the largest platform of ZZS3600 high vacuum coating machine. Properties of the deposited films as well as thickness uniformity were researched. The familiar optics as Ta2O5 and SiO2 were produced by the ion bombardment of MARK Ⅱ ion sources. Several properties related with the optical coatings were analyzed. It suggests that great improvement achieved of the coating structure and properties of the deposited coatings under the condition that the distance between the substrate and the evaporation sources are extremely large. Based on the geometric configurations of the platform, the coating uniformity research of planetary system and single axis coating system were performed, respectively. The thickness nonuniformity is better than 0.4% without mask under the planetary system. As for single axis system, the thickness nonuniformity can be obtained less than 0.6%. High-quality large optical coatings can be acquired with the aid of double ion sources.
- IAD /
- high vacuum coating facilities /
- large optical coating /
- optical properties /
- thickness uniformity

[1]
[2]	James J McNally, Ghanim A Al-Jumaily, John R McNeil, et al. Ion assisted deposition of optical and protective coatings for heavy metal fluoride glass [J]. Applied Optics, 1986, 25(12): 1973-1976.
[3]	Gu Peifu, Chen Yenming, Hu Xuequn, et al. Properties of dielectric coatings produced by ion assisted deposition[J]. Applied Optics, 1989, 28(15): 3318-3322.
[4]
[5]
[6]	Hansjrg N, Sven L, Michael K, et al. Ion-assisted deposition of oxide materials at room temperature by use of different ion sources[J]. Applied Optics, 1999, 38(16): 3610-3613.
[7]	Woo Seouk-Hoon, Chang Kwon Hwangbo. Effects of annealing on the optical, structural, and chemical properties of TiO2 and MgF2 thin films prepared by plasma ion-assisted deposition [J]. Applied Optics, 2006, 45(7): 1447-1455.
[8]
[9]
[10]	Ai Wanjun, Xiong Shengming. Properties of thin films prepared with End-Hall and APS ion assisted deposition[J]. Chinese Journal of Lasers, 2011, 38(11): 1107001. (in Chinese) 艾万君, 熊胜明. End-Hall与APS离子源辅助沉积制备的薄膜特性[J]. 中国激光, 2011, 38(11): 1107001.
[11]
[12]	Culver T R, Pawlewicz W T, Zachistal J H, et al. developments in ion assisted multilayer coatings [C]//SPIE, 1993, 1848: 192-199.
[13]
[14]	Michael L Fulton. Approaches explored for producing a variety of ion-assisted-deposited thin-film coatings using an end-Hall ion source [C]//SPIE, 1996, 2776: 114-125.
[15]
[16]	Michael L Fulton. Application of ion-assisted-deposition using a gridless end-Hall ion source for volume manufacturing of thin-film optical filters [C]//SPIE, 1994, 2253: 374-393.
[17]	Walter T P, Thomas R C, John H Z. Ion assisted evaporative coating of 2-meter optics[C]//SPIE, 1992, 1618: 2-13.
[18]
[19]	Walter T P, Thomas R C, Chiello M W, et al. Low-energy high-flux reactive ion assisted deposition of oxide optical coatings: performance, durability, stability and scalability[C]//SPIE, 1994, 2262: 2-13.
[20]
[21]
[22]	Ritter E. Optical films materials and their applications[J]. Applied Optics, 1976, 15(10): 2318-2327.
[23]	Lee Chengchung, Wan Dershen, Jaing Chengchung, et al. Masking aspherical mirrors by thin-film deposition[J]. Applied Optics, 1993, 32(28): 5535-5540.

[1]	张学海, 魏合理, 段金龙, 李卫东, 邹曙光, 戴聪明. 灰霾期间硫酸盐包裹沙尘气溶胶粒子的光学特性研究 . 红外与激光工程, 2021, 50(11): 20210052-1-20210052-9. doi: 10.3788/IRLA20210052
[2]	黄国俊, 陆益敏, 程勇, 田方涛, 米朝伟, 万强. 脉冲激光沉积法制备红外光学SiC薄膜特性研究 . 红外与激光工程, 2019, 48(7): 742003-0742003(5). doi: 10.3788/IRLA201948.0742003
[3]	程勇, 陆益敏, 黄国俊, 米朝伟, 黎伟, 田方涛, 王赛. 磁场辅助激光沉积类金刚石膜初探 . 红外与激光工程, 2019, 48(11): 1117002-1117002(5). doi: 10.3788/IRLA201948.1117002
[4]	王多书, 李佑路, 李凯朋, 王济洲, 董茂进. 红外光学薄膜材料折射率温度特性的研究方法 . 红外与激光工程, 2018, 47(4): 404006-0404006(5). doi: 10.3788/IRLA201847.0404006
[5]	王利栓, 杨霄, 刘丹丹, 姜承慧, 刘华松, 季一勤, 张锋, 樊荣伟, 陈德应. 离子束溅射氧化钽薄膜光学特性的热处理效应 . 红外与激光工程, 2018, 47(3): 321004-0321004(7). doi: 10.3788/IRLA201847.0321004
[6]	潘永强, 陈佳. 光学薄膜减散射特性研究 . 红外与激光工程, 2016, 45(1): 118007-0118007(5). doi: 10.3788/IRLA201645.0118007
[7]	张圣斌, 左敦稳, 卢文壮. 金刚石衬底的氧化钒薄膜光电特性研究 . 红外与激光工程, 2016, 45(12): 1221001-1221001(8). doi: 10.3788/IRLA201645.1221001
[8]	杨飞, 刘国军, 安其昌. 平差理论在大口径光学元件轮廓检测中的应用 . 红外与激光工程, 2015, 44(10): 2965-2969.
[9]	李宏壮, 赵勇志, 马鑫雪, 于树海, 殷丽梅. 大口径折反式三组元连续变焦距光学系统设计 . 红外与激光工程, 2015, 44(10): 3037-3042.
[10]	杨飞, 刘国军, 安其昌. 结构函数在大口径光学系统评价中的应用 . 红外与激光工程, 2014, 43(11): 3832-3836.
[11]	巫玲, 李佳斌, 陈念年, 熊召, 刘长春, 范勇. 大口径平面光学元件面形检测中激光光斑质心定位 . 红外与激光工程, 2014, 43(6): 1704-1709.
[12]	代福, 熊胜明. 高重复频率DPL 激光对光学薄膜元件损伤实验研究 . 红外与激光工程, 2014, 43(7): 2074-2080.
[13]	刘强, 王贵师, 刘锟, 陈卫东, 朱文越, 黄印博, 高晓明. 基于光声光谱技术的大气气溶胶吸收系数测量 . 红外与激光工程, 2014, 43(9): 3010-3014.
[14]	范世鹏, 林德福, 路宇龙, 宗睿. 激光制导武器半实物仿真系统的设计与实现 . 红外与激光工程, 2014, 43(2): 394-397.
[15]	姜玉刚, 王利栓, 刘华松, 刘丹丹, 姜承慧, 羊亚平, 季一勤. 热处理对SiO₂薄膜折射率和吸收特性的影响分析 . 红外与激光工程, 2014, 43(10): 3334-3337.
[16]	郝宏刚, 周翱, 饶敏, 阮巍. 采用光热失调技术的光学薄膜吸收均匀性测量系统 . 红外与激光工程, 2013, 42(10): 2842-2845.
[17]	刘华松, 傅翾, 王利栓, 姜玉刚, 冷健, 庄克文, 季一勤. 弱吸收单面薄膜光学特性的表征方法 . 红外与激光工程, 2013, 42(8): 2108-2114.
[18]	季一勤, 姜玉刚, 刘华松, 王利栓, 刘丹丹, 姜承慧, 羊亚平, 樊荣伟, 陈德应. 热处理对低损耗高反膜特性的影响分析 . 红外与激光工程, 2013, 42(3): 742-746.
[19]	明名, 杨飞, 赵金宇, 张丽敏, 吴小霞. 折反式大口径、大视场、宽光谱光学系统 . 红外与激光工程, 2012, 41(1): 149-154.
[20]	孙岩, 付秀华, 石澎, 姚林. 红外探测器滤光膜的研究与制备 . 红外与激光工程, 2012, 41(1): 129-132.

点击查看大图

计量

文章访问数: 411
HTML全文浏览量: 55
PDF下载量: 155
被引次数: 0

离子束辅助沉积大口径光学薄膜

1. 中国科学院光电技术研究所,四川成都 610209

作者简介:
艾万君(1985-),男,硕士生,主要从事光学薄膜的制备及其特性方面的研究。Email:awj422177370@163.com

收稿日期: 2015-11-05
修回日期: 2015-12-03
刊出日期: 2016-01-25

中图分类号: O484.4

关键词:

摘要: 利用国内最大箱式高真空镀膜设备ZZS3600,开展了双离子束辅助反应蒸发技术及光学薄膜厚度均匀性研究。借助MarkⅡ离子源辅助反应蒸发技术,对Ta2O5、SiO2常见的高、低折射率光学薄膜进行了制备与特性分析。结果表明:在蒸发源与沉积基底距离较大的镀膜环境下,具有低能、高束流密度离子源有利于薄膜结构的致密化,薄膜性能的改善。根据大口径光学元件尺寸,结合真空室空间几何配置,开展了行星及单轴转动方式下镀膜膜厚均匀性的研究。行星转动方式下,分析了直径140 cm行星盘工件膜厚均匀性,无修正挡板运行时膜厚不均匀性优于0.4%。单轴转动方式下,分析了200 cm光学元件膜厚均匀性,并通过设计修正挡板将膜厚不均匀性控制在0.6%以内。采用双离子束辅助反应蒸发技术有利于实现高性能大口径光学薄膜的制备。