8~14μm波段水性红外隐身涂料研究

叶圣天 成声月 刘朝辉 王飞 贾艺凡

叶圣天, 成声月, 刘朝辉, 王飞, 贾艺凡. 8~14μm波段水性红外隐身涂料研究[J]. 红外与激光工程, 2016, 45(2): 204004-0204004(6). doi: 10.3788/IRLA201645.0204004
引用本文: 叶圣天, 成声月, 刘朝辉, 王飞, 贾艺凡. 8~14μm波段水性红外隐身涂料研究[J]. 红外与激光工程, 2016, 45(2): 204004-0204004(6). doi: 10.3788/IRLA201645.0204004
Ye Shengtian, Cheng Shengyue, Liu Zhaohui, Wang Fei, Jia Yifan. Water-based infrared stealth coating in 8-14μm wavebands[J]. Infrared and Laser Engineering, 2016, 45(2): 204004-0204004(6). doi: 10.3788/IRLA201645.0204004
Citation: Ye Shengtian, Cheng Shengyue, Liu Zhaohui, Wang Fei, Jia Yifan. Water-based infrared stealth coating in 8-14μm wavebands[J]. Infrared and Laser Engineering, 2016, 45(2): 204004-0204004(6). doi: 10.3788/IRLA201645.0204004

8~14μm波段水性红外隐身涂料研究

doi: 10.3788/IRLA201645.0204004
基金项目: 

重庆市自然科学基金(CSTC2012gg-sfgc00002)

详细信息
    作者简介:

    叶圣天(1992-),男,硕士生,主要从事红外隐身材料方面的研究。Email:1129049096@qq.com

  • 中图分类号: TQ637

Water-based infrared stealth coating in 8-14μm wavebands

  • 摘要: 从基体树脂、填料和涂层综合性能三方面对8~14m波段水性红外隐身涂料进行了研究。用红外发射率测量仪测量了涂层在8~14m波段的红外发射率,用红外光谱仪测量了树脂红外吸收图谱,用扫描电镜观察了涂层表面形貌。结果表明,丙烯酸树脂在8~14m波段有较高的红外透明性,适合做涂料基体树脂;铝银浆能在涂层中形成致密的反射层,适合做红外隐身涂料的填料;填料的粒径、含量和形态都对涂层的发射率有较大的影响;选用钢板为基材,以丙烯酸树脂为基体树脂,粒径2000目、浮铝百分比为50%的铝银浆为填料,当涂层中填料含量为15%时,测得其发射率为0.34。
  • [1] Li Bo. Application and development trend of infrared stealth technology[J]. Chinese Optics, 2013, 6(6):818-822.(in Chinese)李波. 红外隐身技术的应用及发展趋势[J]. 中国光学, 2013, 6(6):818-822.
    [2]
    [3] Li Junshan, Chen Xia, Li Jianhua. Infrared radiation characteristics contrast betweem target and background on different grounds[J]. Infrared and Laser Engineering, 2014, 43(2):424-428.(in Chinese)李俊山, 陈霞, 李建华. 不同地面背景下目标与背景红外辐射量对比特性[J]. 红外与激光工程, 2014, 43(2):424-428.
    [4]
    [5] Chen Shiguo, Jiang Yong, Fang Haobai, et al. IR radiation imaging test, process and evaluation of jet aeroengine[J]. Infrared and Laser Engineering, 2014, 43(3):727-731.(in Chinese)陈世国, 江勇, 方浩百, 等. 喷气发动机红外辐射成像测试、处理与评估[J]. 红外与激光工程, 2014, 43(3):727-731.
    [6]
    [7]
    [8] Wang Rui. Compound guided system with active laser imaging and passive infrared imaging[J]. Chinese Optics, 2013, 6(4):536-543.(in Chinese)王锐. 激光红外主被动复合导引系统[J]. 中国光学, 2013, 6(4):536-543.
    [9]
    [10] Yang Ciyin, Cao Lihua, Zhang Jianping. Measurement of infrared radiation for target airplane based on real-time atmospheric correction[J]. Optics and Precision Engineering, 2014, 22(7):1751-1759.(in Chinese)杨词银, 曹立华, 张建萍. 基于大气实时修正的飞机辐射特性测量[J]. 光学精密工程, 2014, 22(7):1751-1759.
    [11]
    [12] Wang Ning. Research on multi-spectral stealth tarpaulin materials[D]. Chongqing:Chongqing University, 2006:4-5.(in Chinese)汪宁. 多频谱隐身篷布材料的研究[D]. 重庆:重庆大学,2006:4-5.
    [13]
    [14] Chen Xuan, Zhang Jian, Wang Yanwu, et al. Infrared stealth technology based on performance parameters of camouflage coating[J]. Optics and Precision Engineering, 2009, 17(2):280-285.(in Chinese)陈翾, 张健, 王艳武, 等. 基于涂料性能参数的红外隐身技术[J]. 光学精密工程, 2009, 17(2):280-285.
    [15]
    [16] Xu Feifeng, Xu Guoyue, Tan Shujuan, et al. Preparation methods of low infrared emissivity and low glossiness coatings for 8-14m wave band[J]. Ordnance Material Science and Engineering, 2011, 34(4):5-9.(in Chinese)徐飞凤, 徐国跃, 谭淑娟, 等. 8~14m波段低红外发射率与低光泽度兼容涂层的制备方法初探[J]. 兵器材料科学与工程, 2011, 34(4):5-9.
    [17]
    [18] Yu H, Xu G, Shen X, et al. Low infrared emissivity of polyurethane/Cu composite coatings[J]. Applied Surface Science, 2009, 255(12):6077-6081.
    [19] Yu H, Xu G, Shen X, et al. Effects of size, shape and floatage of Cu particles on the low infrared emissivity coatings[J]. Progress in Organic Coatings, 2009, 66(2):161-166.
    [20]
    [21]
    [22] Zhang Weigang, Xu Guoyue, Qiao Jialiang, et al. Low emissivity at 8 to 14m and low near-infrared reflective properties of Al-Sm2O3/polyurethane composite coatings[J]. Acta Materiae Compositae Sinica, 2014, 34(2):436-440.(in Chinese)张伟钢, 徐国跃, 乔加亮, 等. Al-Sm2O3/聚氨酯复合涂层的近红外低反射与8~14m低发射率性能[J]. 复合材料学报, 2014, 34(2):436-440.
    [23]
    [24] Li Jingyu, Shi Dongmei. Study on the property of several adhesives for infrared stealth coatings[J]. Modern Paint Finishing, 2010, 13(7):18-20.(in Chinese)李靖宇, 施冬梅. 几种红外隐身涂料黏合剂的性能研究[J]. 现代涂料与涂装, 2010, 13(7):18-20.
    [25]
    [26] Zhang Jianqi. Infrared Physics[M]. Xi'an:Xidian University Press, 2013:60-62.(in Chinese)张建奇. 红外物理[M]. 西安:西安电子科技大学出版社,2013:60-62.
    [27]
    [28] Sun Handong, Fan Zhen, Chang Dading, et al. The road to enhance emissivity of high temperature infrared emissivity coating[J]. Infrared Technology, 1990, 12(3):31-34.(in Chinese)孙汉东, 樊震, 常大定, 等. 提高高温红外辐射涂层发射率的途径[J]. 红外技术, 1990, 12(3):31-34.
    [29] Liu Lingyun, Gong Rongzhou, Nie Yan, et al. Computation model of the thermal infrared emittance of a coating[J]. Acta Photonica Sinica, 2006, 35(12):1903-1907.(in Chinese)刘凌云, 龚荣洲, 聂彦, 等. 涂层的热红外发射率计算模型[J]. 光子学报, 2006, 35(12):1903-1907.
    [30]
    [31]
    [32] Liu Xiaodong, Dai Jingmin. Measurement of the complex refractive index of particles based on Mie theory index and transmission method[J]. Infrared and Laser Engineering, 2009, 38(5):820-824.(in Chinese)刘晓东, 戴景民. Mie散射理论测量粒子系复折射率的透射方法[J]. 红外与激光工程, 2009, 38(5):820-824.
    [33] Ren Yue, Hua Ping, Gong Rongzhou. Materials with low infrared emissivity based on epoxy resin[J]. Ordnance Material Science and Engineering, 2011, 34(2):45-48.(in Chinese)任玥, 华萍, 龚荣洲. 基于环氧树脂的低红外发射率材料研究[J]. 兵器材料科学与工程, 2011, 34(2):45-48.
  • [1] 高荣, 毛祥龙, 李锦鹏, 徐志晨, 谢永军.  自由曲面离轴四反全铝光机红外探测系统(特邀) . 红外与激光工程, 2023, 52(7): 20230338-1-20230338-11. doi: 10.3788/IRLA20230338
    [2] 沈文力, 谭秋林, 张磊, 谢浩.  基于硫系玻璃-聚甲基丙烯酸甲酯分光结构的散斑计算重组光谱仪设计 . 红外与激光工程, 2023, 52(10): 20230038-1-20230038-9. doi: 10.3788/IRLA20230038
    [3] 姜鑫鹏, 杜特, 马汉斯, 张兆健, 何新, 张振福, 陈欢, 于洋, 黄沙, 杨俊波.  光学微纳结构红外隐身技术研究进展(特邀) . 红外与激光工程, 2023, 52(6): 20230197-1-20230197-14. doi: 10.3788/IRLA20230197
    [4] 陈苏麒, 单勇, 张靖周, 杨宗耀.  挡板构型对直升机红外抑制器气动与红外辐射特性影响研究 . 红外与激光工程, 2022, 51(8): 20210659-1-20210659-13. doi: 10.3788/IRLA20210659
    [5] 于鲲, 段雨晗, 丛明煜, 戴文聪.  飞行器红外物理成像仿真优化计算方法 . 红外与激光工程, 2021, 50(4): 20200241-1-20200241-14. doi: 10.3788/IRLA20200241
    [6] 褚宏晨, 赖耘.  基于超表面的超薄隐身器件 . 红外与激光工程, 2020, 49(9): 20201038-1-20201038-8. doi: 10.3788/IRLA20201038
    [7] 赵晓枫, 魏银鹏, 杨佳星, 蔡伟, 张志利.  综合相似性在红外目标隐身效果评估中的应用 . 红外与激光工程, 2020, 49(1): 0104004-0104004(11). doi: 10.3788/IRLA202049.0104004
    [8] 曹飞飞, 吉洪湖, 于明飞, 吴开军.  低发射率材料涂敷区域对排气系统壁温和红外特性的影响 . 红外与激光工程, 2020, 49(10): 20190131-1-20190131-9. doi: 10.3788/IRLA20190131
    [9] 王超哲, 李慎波, 黄聪会, 柴世杰, 贾文铜.  飞机成像目标的红外隐身效果评估 . 红外与激光工程, 2019, 48(10): 1004004-1004004(9). doi: 10.3788/IRLA201948.1004004
    [10] 张冬晓, 何永强, 胡文刚, 陈一超.  自适应红外隐身系统的背景投影建模 . 红外与激光工程, 2016, 45(3): 304001-0304001(7). doi: 10.3788/IRLA201645.0304001
    [11] 李文胜, 张琴, 付艳华, 黄海铭.  一种基于光子晶体结构的军用车辆红外隐身涂层的设计 . 红外与激光工程, 2015, 44(11): 3299-3303.
    [12] 黄伟, 吉洪湖.  蒙皮反射的背景辐射对亚声速飞机红外特征的影响研究(二): 应用 . 红外与激光工程, 2015, 44(7): 2039-2043.
    [13] 成声月, 刘朝辉, 叶圣天, 王飞, 贾艺凡, 班国东.  水性红外迷彩涂料的制备及其表征 . 红外与激光工程, 2015, 44(8): 2298-2304.
    [14] 林涛, 刘飞, 韩平丽, 邵晓鹏, 任勐, 吕鸿鹏, 张建奇.  中波红外隐身目标光谱探测的谱带选择方法 . 红外与激光工程, 2014, 43(4): 1047-1051.
    [15] 陈世国, 江勇, 方浩百, 李卒.  喷气发动机红外辐射成像测试、处理与评估 . 红外与激光工程, 2014, 43(3): 727-731.
    [16] 蒋治国.  减弱激光回波的隐身技术 . 红外与激光工程, 2013, 42(8): 2032-2035.
    [17] 桑建华, 张宗斌.  红外隐身技术发展趋势 . 红外与激光工程, 2013, 42(1): 14-19.
    [18] 杜永成, 杨立, 张士成.  细水雾遮蔽红外辐射的数值分析 . 红外与激光工程, 2013, 42(8): 1967-1972.
    [19] 徐顶国, 桑建华, 罗明东.  无人机蒙皮红外辐射特征研究 . 红外与激光工程, 2013, 42(4): 880-884.
    [20] 陈叔平, 谢福寿, 谭风光, 温永刚, 陈光奇.  空间冷屏表面温度分布实验研究 . 红外与激光工程, 2012, 41(6): 1411-1415.
  • 加载中
计量
  • 文章访问数:  540
  • HTML全文浏览量:  114
  • PDF下载量:  261
  • 被引次数: 0
出版历程
  • 收稿日期:  2015-06-17
  • 修回日期:  2015-07-03
  • 刊出日期:  2016-02-25

8~14μm波段水性红外隐身涂料研究

doi: 10.3788/IRLA201645.0204004
    作者简介:

    叶圣天(1992-),男,硕士生,主要从事红外隐身材料方面的研究。Email:1129049096@qq.com

基金项目:

重庆市自然科学基金(CSTC2012gg-sfgc00002)

  • 中图分类号: TQ637

摘要: 从基体树脂、填料和涂层综合性能三方面对8~14m波段水性红外隐身涂料进行了研究。用红外发射率测量仪测量了涂层在8~14m波段的红外发射率,用红外光谱仪测量了树脂红外吸收图谱,用扫描电镜观察了涂层表面形貌。结果表明,丙烯酸树脂在8~14m波段有较高的红外透明性,适合做涂料基体树脂;铝银浆能在涂层中形成致密的反射层,适合做红外隐身涂料的填料;填料的粒径、含量和形态都对涂层的发射率有较大的影响;选用钢板为基材,以丙烯酸树脂为基体树脂,粒径2000目、浮铝百分比为50%的铝银浆为填料,当涂层中填料含量为15%时,测得其发射率为0.34。

English Abstract

参考文献 (33)

目录

    /

    返回文章
    返回