激光沉积修复ZL114A铝合金的显微组织及显微硬度研究

钦兰云 庞爽 杨光 王超 王维

钦兰云, 庞爽, 杨光, 王超, 王维. 激光沉积修复ZL114A铝合金的显微组织及显微硬度研究[J]. 红外与激光工程, 2017, 46(5): 506004-0506004(6). doi: 10.3788/IRLA201746.0506004
引用本文: 钦兰云, 庞爽, 杨光, 王超, 王维. 激光沉积修复ZL114A铝合金的显微组织及显微硬度研究[J]. 红外与激光工程, 2017, 46(5): 506004-0506004(6). doi: 10.3788/IRLA201746.0506004
Qin Lanyun, Pang Shuang, Yang Guang, Wang Chao, Wang Wei. Microstructure and micro-hardness of laser deposition repair ZL114A aluminum alloy[J]. Infrared and Laser Engineering, 2017, 46(5): 506004-0506004(6). doi: 10.3788/IRLA201746.0506004
Citation: Qin Lanyun, Pang Shuang, Yang Guang, Wang Chao, Wang Wei. Microstructure and micro-hardness of laser deposition repair ZL114A aluminum alloy[J]. Infrared and Laser Engineering, 2017, 46(5): 506004-0506004(6). doi: 10.3788/IRLA201746.0506004

激光沉积修复ZL114A铝合金的显微组织及显微硬度研究

doi: 10.3788/IRLA201746.0506004
基金项目: 

国家自然科学基金(51505301,51305280,51375316);辽宁省自然科学基金(2015020118)

详细信息
    作者简介:

    钦兰云(1977-),女,副教授,博士,主要从事激光沉积成形、修复方面的研究。Email:qinly@sau.edu.cn

  • 中图分类号: TG146.2

Microstructure and micro-hardness of laser deposition repair ZL114A aluminum alloy

  • 摘要: 为了研究激光沉积技术修复ZL114A铝合金构件的工艺及性能,采用多参数组合激光沉积工艺实验制备了单道单层试样,在分析了其表面形貌、气孔等缺陷产生的原因的基础上,得到了一组相对优化的工艺参数,制备了无缺陷的块状修复试样,并对试样进行了组织分析及硬度检测。结果表明:铝合金修复试样修复区与基材形成良好的冶金结合,沉积层底部为以熔池边缘为起点外延生长的柱状树枝晶,且一次枝晶间距18。38 m,二次枝晶间距9。55 m,在沉积层顶层顶部出现-Al柱状枝晶转变为等轴枝晶现象。层带区域Si相脱溶析出并趋于粒状化。由于晶粒细化和固溶强化作用,沉积区显微硬度较基材提高25。8%。
  • [1] Ma Siqun, Gu Lixiang, Yuan Yongwen, et al. Research on influence of welding defects on fatigue life of EMU aluminum-alloy car body[J]. Journal of the China Railway Society, 2014, 36(2):42-48. (in Chinese)马思群, 谷理想, 袁永文, 等. 焊接缺陷对动车组铝合金车体疲劳寿命影响研究[J]. 铁道学报, 2014, 36(2):42-48.
    [2] Casalino G, Mortello M, Paola Leo, et al. Study on arc and laser powers in the hybrid welding of AA574 Al-alloy[J]. Materials and Design, 2014, 61:191-198.
    [3] Lin Xin, Huang Weidong. High-performance laser gain material of metal components manufacturing[J]. Scientia Sinica Informationis, 2015, 45(9):1111-1126. (in Chinese)林鑫,黄卫东. 高性能金属构件的激光增材制造[J]. 中国科学:信息学, 2015, 45(9):1111-1126.
    [4] Wang Huaming. Materials fundamental issues of laser additive manufacturing for high-performance large metallic components[J]. Acta Aeronautic et Astronautica Sinica, 2014, 35(10):2690-2698. (in Chinese)王华明. 高性能大型金属构件激光增材制造:若干材料基础问题[J]. 航空学报, 2014, 35(10):2690-2698.
    [5] Watkins K G, McMahon M A, Streen W M. Microstructure and corrosion properties of laser surface processed aluminium alloys:a review[J]. Materials Science and Engineering A, 1997, 231(1-2):55-61.
    [6] Zhuang W, Liu Q, Djugum R, et al. Deep surface rolling for fatigue life enhancement of laser clad aircraft aluminium alloy[J]. Applied Surface Science, 2014, 320:558-562.
    [7] Ehsan Toyserkani, Stephen Corbin, Amir Khajepour. Laser Cladding[M]. New York:CRC Press, 2005.
    [8] Wang Xiaoyan, Chen Jing, Lin Xin, et al. Microstructure of laser forming repair 7050 aluminum alloy with AlSi12 powder[J]. Chinese of Journal of Lasers, 2009, 36(6):1585-1590. (in Chinese)王小艳, 陈静, 林鑫, 等. AlSi12粉激光成形修复7050铝合金组织[J]. 中国激光, 2009, 36(6):1585-1590.
    [9] Xue Lei, Huang Yixiong, Lu Penghui, et al. Study on microstructure and property of laser forming repaired ZL104 alloy[J]. China Surface Engineering, 2010, 23(1):97-100. (in Chinese)薛蕾, 黄一雄, 卢鹏辉, 等. 激光成形修复ZL104合金的组织与性能研究[J]. 中国表面工程, 2010, 23(1):97-100.
    [10] Zuo Tiechuan. Laser Material Processing of High Strength Aluminum Alloy[M]. Beijing:National Defence Industry Press, 2002:2-10. (in Chinese)左铁钏. 高强铝合金的激光加工[M]. 北京:国防工业出版社, 2002:2-10.
    [11] Chen Xiaoming, Song Renguo, Zhang Yu, et al. Effects of overfire on microstructure and properties of 7003 aluminum alloy[J]. Light Alloy Fabrication Technology, 2009, 37(2):48-52. (in Chinese)陈小明, 宋仁国, 张宇, 等. 过烧对7003铝合金组织与性能的影响[J]. 轻合金加工技术, 2009, 37(2):48-52.
    [12] Zhou Wansheng, Yao Junshan. The Welding of Aluminium and Aluminium Alloy[M]. Beijing:China Machine Press, 2007:40-46. (in Chinese)周万盛, 姚军山. 铝及铝合金的焊接[M]. 北京:机械工业出版社, 2007:40-46.
    [13] Huang Weidong. Laser Solid Forming[M]. Xi' an:Northwestern Polytechnical University Press, 2007:57-60. (in Chinese)黄卫东. 激光立体成形[M]. 西安:西北工业大学出版社, 2007:57-60.
    [14] Shi Lei, Wang Youqi, Wang Ying, et al. Effect of solution treatment on microstructure and mechanical properties of quasi eutectivc Al-Si Alloy[J]. The Chinese Journal of Nonferrous Metals, 2012, 22(12):3372-3377. (in Chinese)石磊, 王有祁, 王英, 等. 固溶处理对准共晶Al-Si合金显微组织及力学性能影响[J]. 中国有色金属学报, 2012, 22(12):3372-3377.
    [15] Chen Yongcheng, Zhang Shuquan, Tian Xiangjun, et al. Microstructure and microhardness of 4045 aluminium alloy fabricated by laser melting deposition.[J]. Chinese of Journal of Lasers, 2015, 42(3):0303008. (in Chinese)陈永城, 张述泉, 田象军, 等. 激光熔化沉积4045铝合金显微组织及显微硬度[J]. 中国激光, 2015, 42(3):0303008.
    [16] Wang Aiqin, Xie Jingpei, Liu Zhongxia, et al. Microstructure and phase structure of rapidly solidified Al-Si alloy[J]. Transactions of Materials and Heat Treatment, 2008, 29(2):99-102. (in Chinese)王爱琴, 谢敬佩, 刘忠侠, 等. 快速凝固Al-Si合金的组织形态及相结构[J]. 材料热处理学报, 2008, 29(2):99-102.
  • [1] 卞宏友, 徐效文, 刘伟军, 王蔚, 邢飞, 王慧儒.  激光沉积修复DD5合金的枝晶外延生长控制与显微组织特征 . 红外与激光工程, 2023, 52(5): 20220731-1-20220731-13. doi: 10.3788/IRLA20220731
    [2] 巴一, 韩善果, 杨永强, 郑世达, 师文庆.  激光摆动路径对钢/铝点焊接头组织与性能的影响 . 红外与激光工程, 2022, 51(8): 20210799-1-20210799-10. doi: 10.3788/IRLA20210799
    [3] 邱星武.  激光熔覆Fe0.5NiCoCrCuTi高熵合金涂层的微观结构及性能 . 红外与激光工程, 2019, 48(7): 742004-0742004(8). doi: 10.3788/IRLA201948.0742004
    [4] 徐洋洋, 周建忠, 谭文胜, 孟宪凯, 盛杰, 黄舒, 孙昀杰.  深冷激光喷丸强化2024-T351铝合金的表面力学性能 . 红外与激光工程, 2018, 47(12): 1206002-1206002(8). doi: 10.3788/IRLA201847.1206002
    [5] 卞宏友, 翟泉星, 曲伸, 杨光, 王伟, 王维.  GH738合金激光沉积修复试验研究 . 红外与激光工程, 2018, 47(7): 706002-0706002(6). doi: 10.3788/IRLA201847.0706002
    [6] 邱星武, 吴明军, 戚燕, 刘春阁, 张云鹏, 黄崇湘.  激光熔覆Al2CrFeCoCuNixTi高熵合金涂层的组织及耐蚀性能 . 红外与激光工程, 2018, 47(7): 706008-0706008(8). doi: 10.3788/IRLA201847.0706008
    [7] 王学德, 罗思海, 何卫锋, 聂祥樊, 焦阳.  无保护层激光冲击对K24镍基合金力学性能的影响 . 红外与激光工程, 2017, 46(1): 106005-0106005(6). doi: 10.3788/IRLA201746.0106005
    [8] 王彦芳, 李豪, 石志强, 肖亚梅, 孙旭, 王亭.  激光熔覆高耐蚀Fe基固溶体合金涂层 . 红外与激光工程, 2017, 46(8): 806001-0806001(5). doi: 10.3788/IRLA201746.0806001
    [9] 杨光, 王文东, 钦兰云, 任宇航, 李长富, 王维.  退火温度及保温时间对激光沉积制造TA15钛合金微观组织和显微硬度的影响 . 红外与激光工程, 2017, 46(8): 806006-0806006(6). doi: 10.3788/IRLA201746.0806006
    [10] 杨光, 刘欢欢, 周佳平, 钦兰云, 王维, 任宇航.  激光沉积修复某型飞机垂尾梁研究 . 红外与激光工程, 2017, 46(2): 206004-0206004(9). doi: 10.3788/IRLA201746.0206004
    [11] 卞宏友, 赵翔鹏, 李英, 杨光, 钦兰云, 王维, 任宇航.  激光沉积修复GH4169合金试验研究 . 红外与激光工程, 2016, 45(2): 206006-0206006(6). doi: 10.3788/IRLA201645.0206006
    [12] 卞宏友, 雷洋, 李英, 杨光, 钦兰云, 王维, 韩双隆.  感应预热对激光沉积修复TA15钛合金显微组织和残余应力的影响 . 红外与激光工程, 2016, 45(7): 705003-0705003(6). doi: 10.3788/IRLA201645.0705003
    [13] 焦阳, 何卫锋, 孙岭, 周留成, 聂祥樊, 罗思海, 李靖.  激光喷丸与渗铝复合工艺提高K417 合金力学性能研究 . 红外与激光工程, 2015, 44(8): 2274-2279.
    [14] 王维, 刘奇, 杨光, 钦兰云, 岳耀猛.  电磁搅拌辅助钛合金激光沉积修复的电磁场模拟与验证 . 红外与激光工程, 2015, 44(9): 2666-2671.
    [15] 王维, 李新宇, 杨光, 钦兰云, 任宇航.  超声场下激光沉积TA15钛合金的组织和力学性能 . 红外与激光工程, 2015, 44(12): 3559-3564.
    [16] 唐淑君, 刘洪喜, 张晓伟, 王传琦, 蔡川雄, 蒋业华.  H13钢表面激光选区熔覆Ni-Al金属间化合物涂层的组织与性能 . 红外与激光工程, 2014, 43(5): 1621-1626.
    [17] 李靖, 李军, 何卫锋, 李玉琴, 聂祥樊, 何光宇.  TC17 钛合金激光多次冲击强化后组织和力学性能研究 . 红外与激光工程, 2014, 43(9): 2889-2895.
    [18] 王维, 郭鹏飞, 杨光, 钦兰云, 卞宏友, 王伟, 任宇航.  超声波对BT20钛合金激光沉积修复作用机制探究 . 红外与激光工程, 2014, 43(8): 2453-2459.
    [19] 钦兰云, 王婷, 杨光, 王维, 卞宏友, 任宇航.  激光沉积修复BT20合金试验研究 . 红外与激光工程, 2014, 43(2): 404-410.
    [20] 王传琦, 刘洪喜, 周荣, 蒋业华, 张晓伟.  机械振动辅助激光重熔Ni基合金TiC复合涂层微观组织研究 . 红外与激光工程, 2013, 42(10): 2651-2657.
  • 加载中
计量
  • 文章访问数:  380
  • HTML全文浏览量:  63
  • PDF下载量:  99
  • 被引次数: 0
出版历程
  • 收稿日期:  2016-09-06
  • 修回日期:  2016-10-10
  • 刊出日期:  2017-05-25

激光沉积修复ZL114A铝合金的显微组织及显微硬度研究

doi: 10.3788/IRLA201746.0506004
    作者简介:

    钦兰云(1977-),女,副教授,博士,主要从事激光沉积成形、修复方面的研究。Email:qinly@sau.edu.cn

基金项目:

国家自然科学基金(51505301,51305280,51375316);辽宁省自然科学基金(2015020118)

  • 中图分类号: TG146.2

摘要: 为了研究激光沉积技术修复ZL114A铝合金构件的工艺及性能,采用多参数组合激光沉积工艺实验制备了单道单层试样,在分析了其表面形貌、气孔等缺陷产生的原因的基础上,得到了一组相对优化的工艺参数,制备了无缺陷的块状修复试样,并对试样进行了组织分析及硬度检测。结果表明:铝合金修复试样修复区与基材形成良好的冶金结合,沉积层底部为以熔池边缘为起点外延生长的柱状树枝晶,且一次枝晶间距18。38 m,二次枝晶间距9。55 m,在沉积层顶层顶部出现-Al柱状枝晶转变为等轴枝晶现象。层带区域Si相脱溶析出并趋于粒状化。由于晶粒细化和固溶强化作用,沉积区显微硬度较基材提高25。8%。