CVD-ZnS胞状生长现象抑制方法

杨德雨,  杨海,  李红卫,  霍承松,  魏乃光,  黎建明,  李冬旭,  史晶晶

downloadPDF
文章导航 > 红外与激光工程  > 2018 >  47(11): 1121001-1121001(6)
杨德雨, 杨海, 李红卫, 霍承松, 魏乃光, 黎建明, 李冬旭, 史晶晶. CVD-ZnS胞状生长现象抑制方法[J]. 红外与激光工程, 2018, 47(11): 1121001-1121001(6). doi: 10.3788/IRLA201847.1121001
引用本文: 杨德雨, 杨海, 李红卫, 霍承松, 魏乃光, 黎建明, 李冬旭, 史晶晶. CVD-ZnS胞状生长现象抑制方法[J]. 红外与激光工程, 2018, 47(11): 1121001-1121001(6). doi: 10.3788/IRLA201847.1121001
shu
Yang Deyu, Yang Hai, Li Hongwei, Huo Chengsong, Wei Naiguang, Li Jianming, Li Dongxu, Shi Jingjing. Counteracting methods of nodular growth in CVD-ZnS[J]. Infrared and Laser Engineering, 2018, 47(11): 1121001-1121001(6). doi: 10.3788/IRLA201847.1121001
Citation: Yang Deyu, Yang Hai, Li Hongwei, Huo Chengsong, Wei Naiguang, Li Jianming, Li Dongxu, Shi Jingjing. Counteracting methods of nodular growth in CVD-ZnS[J]. Infrared and Laser Engineering, 2018, 47(11): 1121001-1121001(6). doi: 10.3788/IRLA201847.1121001
shu

CVD-ZnS胞状生长现象抑制方法

doi: 10.3788/IRLA201847.1121001
  • 1.

    北京有色金属研究总院 有研国晶辉新材料有限公司,河北 三河 065201;

  • 2.

    北京有色金属研究总院 有研新材料有限公司,北京 100088

详细信息
    作者简介:

    杨德雨(1992-),男,硕士生,主要从事CVD-ZnS晶体异常生长现象方面的研究。Email:csuyangdeyu@163.com

  • 中图分类号: TN213

Counteracting methods of nodular growth in CVD-ZnS

  • 1.

    GRIREM Guojing Advanced Material Co.,Ltd.,General Research Institute for Nonferrous Metals,Sanhe 065201,China;

  • 2.

    GRIREM Advanced Materials Co.,Ltd.,General Research Institute for Nonferrous Metals,Beijing 100088,China

  • 摘要: 实验采用化学气相沉积方法制备硫化锌体材料（CVD-ZnS），并对材料中普遍出现的胞状生长现象进行了系统研究。通过微观结构表征及宏观形貌分析，发现胞状生长起始于大尺寸的晶体生长中心，其内部晶粒的生长方向发生了横向偏移，且生长速率大于正常晶粒，最终导致了产物表面的球状凸起，产物侧剖面表现出倒圆锥状生长形貌。同时，依据实验中所出现的不同胞状生长现象，探究了胞状物异常生长中心形成的主要原因。在此基础之上，设计了不同条件的沉积实验，探究了各类胞状生长现象的抑制方法，并在实际生产过程中得到了验证，从而实现了对该异常现象的有效抑制。
    Abstract: Chemical vapor deposition method was used to manufacture bulk ZnS materials (CVD-ZnS). Nodular growth phenomenon in bulk CVD-ZnS was studied systematically. Through the analysis of microstructure and macrostructure, some growth centers with larger size were seen as the origin of nodular cells. Growth direction of nodular cells was changed to cross direction, while growth rate of nodular cells was faster than other normal grains. All of these factors led to the spherical objects on the surface of products. A turbinate structure was observed from nodular cell in cut-plane samples as well. Meanwhile, according to the different nodular phenomena, the main mechanisms of different growth centers were discussed. The counteracting methods, based on above conclusions, were explored and confirmed through different deposited experiments. Thus, the nodular growth in CVD-ZnS could be restrained effectively.
  • [1] Yu Huaizhi. Infrared Optical Materials[M]. Beijing:National Defense Industry Press, 2015. (in Chinese)
    [2] Harris D C. Development of hot pressed and chemical-vapor-deposited zinc sulfide and zinc selenide in the united states for optical windows[C]//SPIE, 2007, 6545:654502.
    [3] Donadio R N, Connolly J F, Taylor R L. New advances in chemical vapor deposited(CVD) infrared transmitting materials[C]//SPIE, 1982, 297(12):65-69.
    [4] Fu Ligang, Huo Chengsong, Zhang Fuchang, et al. Form mechanism and restrain method of hexagonal in CVDZnS[J]. Infrared and Laser Engineering, 2010, 39(6):1100-1104. (in Chinese)
    [5] Fu Ligang, Huo Chengsong, Zhang Fuchang, et al. Analysis of microcosmic defects in CVDZnS[J]. Infrared and Laser Engineering, 2012, 41(1):139-143. (in Chinese)
    [6] McCloy J, Eric F, Ralph K, et al. Anisotropy in structural and optical properties of chemical vapor deposited ZnS[C]//SPIE, 2011, 8007:80070K.
    [7] Goela J S, Taylor R L. Monolithic material fabrication by chemical vapor deposition[J]. J Mater Sci, 1988, 23(12):4331-4339.
    [8] McCloy J, Randal T. Chemical Vapor Deposited Zinc-sulfide[M]. Washington:SPIE, 2013:74-76.
    [9] Huo Chengsong, Yang Hai, Fu Ligang. Fabrication of large diameter multi-spectrum ZnS dome[J]. Infrared and Laser Engineering, 2008, 37(4):719-722. (in Chinese)
    [10] Tilman Z, Wolfgan W, Christian R. Microstructure and texture of polycrystalline CVD-ZnS analyzed via EBSD[J]. Adv Funct Mater, 2012, 22(23):4969-4974.
    [11] Fu Ligang. Research on preparation technics and crystal constructure, defects of chemical vapor deposition ZnS[D]. Beijing:University of Science and Technology Beijing, 2010:52-53. (in Chinese)
    [12] Fu Ligang, Huo Chengsong, Zhang Fuchang. Effect of technical parameters on bowing of CVD-ZnS[J]. Journal of Synthetic Crystals, 2010, 39(6):1596-1600. (in Chinese)
  • [1] 王嘉业, 李艺璇, 张玉珍.  基于学习的光栅图像噪声抑制方法 . 红外与激光工程, 2022, 51(2): 20220006-1-20220006-10. doi: 10.3788/IRLA20220006
    [2] 苗效方, 吴鹏, 赵保银.  梳状大模场光纤结构的优化设计 . 红外与激光工程, 2019, 48(9): 918005-0918005(6). doi: 10.3788/IRLA201948.0918005
    [3] 邱星武.  激光熔覆Fe0.5NiCoCrCuTi高熵合金涂层的微观结构及性能 . 红外与激光工程, 2019, 48(7): 742004-0742004(8). doi: 10.3788/IRLA201948.0742004
    [4] 徐美芳, 丁俊文, 王冠军, 张秀丽, 赵英亮.  角度多样性激光散斑抑制方法的比较 . 红外与激光工程, 2017, 46(8): 806004-0806004(6). doi: 10.3788/IRLA201746.0806004
    [5] 李贺, 邓学文, 朱奎宝, 邓年茂.  光纤陀螺抑制过调制串扰的多态方波调制方法 . 红外与激光工程, 2017, 46(8): 822004-0822004(7). doi: 10.3788/IRLA201746.0822004
    [6] 杨永清, 梁雁冰, 李治国, 梁冬生.  基于光纤陀螺的转台周期性误差抑制方法 . 红外与激光工程, 2015, 44(6): 1898-1903.
    [7] 陈庚, 谭晓茗, 单勇, 张靖周.  二元弯曲混合管出口结构参数对红外抑制器气动和辐射特性的影响 . 红外与激光工程, 2015, 44(6): 1704-1711.
    [8] 陈庚, 单勇, 谭晓茗, 张靖周.  混合管结构参数对抑制器气动和红外辐射影响 . 红外与激光工程, 2015, 44(12): 3597-3603.
    [9] 郝立超, 陈洪雷, 李辉, 陈义强, 赖灿雄, 黄爱波, 丁瑞军.  具有记忆功能背景抑制结构的共享型读出电路 . 红外与激光工程, 2015, 44(11): 3293-3298.
    [10] 闫佩佩, 李刚, 刘凯, 姜凯, 段晶, 单秋莎.  不同结构地基光电探测系统的杂散光抑制 . 红外与激光工程, 2015, 44(3): 917-922.
    [11] 钱伟新, 王婉丽, 祁双喜, 程晋明, 刘冬兵.  基于广义变分正则化的红外图像噪声抑制方法 . 红外与激光工程, 2014, 43(1): 67-71.
    [12] 许芃, 李东光, 靳佰良.  采用区域生长和EMDs模型的运动目标检测方法 . 红外与激光工程, 2014, 43(10): 3486-3491.
    [13] 葛广一, 魏振忠.  图像去雾过程中的噪声抑制方法 . 红外与激光工程, 2014, 43(8): 2765-2771.
    [14] 王衍行, 祖成奎, 陈江, 韩滨, 赵慧峰.  钡镓锗透明微晶玻璃的制备及性能 . 红外与激光工程, 2014, 43(5): 1401-1405.
    [15] 王凯, 田长栋, 施清平, 王利威, 段发阶, 张敏, 廖延彪.  抑制光纤检波器系统光强波动影响的解调方法 . 红外与激光工程, 2013, 42(6): 1593-1600.
    [16] 杜磊, 赵剡.  激波辐射对红外成像探测影响的抑制方法研究 . 红外与激光工程, 2013, 42(3): 562-568.
    [17] 徐正平, 张雪菲, 李清军, 李友一, 许永森.  全景式航空相机摄影起始角误差抑制方法 . 红外与激光工程, 2013, 42(8): 2055-2059.
    [18] 吴坤, 张合新, 孟飞, 陈聪.  激光主动成像图像噪声抑制方法 . 红外与激光工程, 2013, 42(9): 2397-2402.
    [19] 梁善勇, 张伟, 王江安, 吴荣华, 马治国.  舰船尾流共轴激光雷达近场抑制比的计算方法 . 红外与激光工程, 2012, 41(8): 2063-2067.
    [20] 付利刚, 霍承松, 张福昌, 魏乃光, 王学武, 吕反修.  CVDZnS微观缺陷分析 . 红外与激光工程, 2012, 41(1): 139-143.
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  440
  • HTML全文浏览量:  103
  • PDF下载量:  29
  • 被引次数: 0
出版历程
  • 收稿日期:  2018-06-10
  • 修回日期:  2018-07-20
  • 刊出日期:  2018-11-25

CVD-ZnS胞状生长现象抑制方法

doi: 10.3788/IRLA201847.1121001
  • 1. 北京有色金属研究总院 有研国晶辉新材料有限公司,河北 三河 065201;
  • 2. 北京有色金属研究总院 有研新材料有限公司,北京 100088
    • 作者简介:

    杨德雨(1992-),男,硕士生,主要从事CVD-ZnS晶体异常生长现象方面的研究。Email:csuyangdeyu@163.com

  • 收稿日期: 2018-06-10
  • 修回日期: 2018-07-20
  • 刊出日期: 2018-11-25

  • 中图分类号: TN213

摘要: 实验采用化学气相沉积方法制备硫化锌体材料（CVD-ZnS），并对材料中普遍出现的胞状生长现象进行了系统研究。通过微观结构表征及宏观形貌分析，发现胞状生长起始于大尺寸的晶体生长中心，其内部晶粒的生长方向发生了横向偏移，且生长速率大于正常晶粒，最终导致了产物表面的球状凸起，产物侧剖面表现出倒圆锥状生长形貌。同时，依据实验中所出现的不同胞状生长现象，探究了胞状物异常生长中心形成的主要原因。在此基础之上，设计了不同条件的沉积实验，探究了各类胞状生长现象的抑制方法，并在实际生产过程中得到了验证，从而实现了对该异常现象的有效抑制。