磁场辅助激光沉积类金刚石膜初探

程勇,  陆益敏,  黄国俊,  米朝伟,  黎伟,  田方涛,  王赛

downloadPDF
文章导航 > 红外与激光工程  > 2019 >  48(11): 1117002-1117002(5)
程勇, 陆益敏, 黄国俊, 米朝伟, 黎伟, 田方涛, 王赛. 磁场辅助激光沉积类金刚石膜初探[J]. 红外与激光工程, 2019, 48(11): 1117002-1117002(5). doi: 10.3788/IRLA201948.1117002
引用本文: 程勇, 陆益敏, 黄国俊, 米朝伟, 黎伟, 田方涛, 王赛. 磁场辅助激光沉积类金刚石膜初探[J]. 红外与激光工程, 2019, 48(11): 1117002-1117002(5). doi: 10.3788/IRLA201948.1117002
shu
Cheng Yong, Lu Yimin, Huang Guojun, Mi Chaowei, Li Wei, Tian Fangtao, Wang Sai. Pre-research on the diamond-like carbon film prepared by magnet-assistant pulsed laser deposition[J]. Infrared and Laser Engineering, 2019, 48(11): 1117002-1117002(5). doi: 10.3788/IRLA201948.1117002
Citation: Cheng Yong, Lu Yimin, Huang Guojun, Mi Chaowei, Li Wei, Tian Fangtao, Wang Sai. Pre-research on the diamond-like carbon film prepared by magnet-assistant pulsed laser deposition[J]. Infrared and Laser Engineering, 2019, 48(11): 1117002-1117002(5). doi: 10.3788/IRLA201948.1117002
shu

磁场辅助激光沉积类金刚石膜初探

doi: 10.3788/IRLA201948.1117002
  • 1.

    陆军工程大学 光电技术研究所,湖北 武汉 430075

基金项目: 

军内科研项目（012016017000B12503）

详细信息
    作者简介:

    程勇(1961-),男,教授,所长,博士,主要从事激光技术及其应用方面的研究。Email:gdyjs@263.net

    通讯作者: 陆益敏(1981-),男,讲师,博士,主要从事脉冲激光沉积功能薄膜方面的研究。Email:luyimin_zy@163.com

  • 中图分类号: TN304.2

Pre-research on the diamond-like carbon film prepared by magnet-assistant pulsed laser deposition

  • 1.

    Opto-Electronics Institute,Army Engineering University,Wuhan 430075,China

  • 摘要: 提出了磁场辅助激光沉积类金刚石（DLC）膜技术，在硅基底附近添加磁力线向基底收拢的磁场，用以迫使侧向飞行的离子向基底靠拢并参与成膜。由于离子向基底的集中，使其在膜层中含量大幅上升，间接地减少了大颗粒的比例，因此，与无磁场条件下制备的DLC膜相比，引入磁场不仅提高了DLC膜的沉积速率，而且提高了其机械硬度；更重要的是，间接地证明了激光对靶材离化的高效性，为脉冲激光沉积（PLD）结合磁过滤技术提供了可行性的依据。
    Abstract: The technology of magnet-assistant pulsed laser deposition was advanced. A magnetic field whose magnetic lines pointed to the substrate was fixed around the silicon substrate when the diamondlike carbon(DLC) film was prepared by pulsed laser deposition(PLD), so that the ions those flied outside of the substrate were drove to fly to the substrate potentially and participate in the course of filming. The concentration of the ions increased based on the centralization of the ions, and the content of the non-electriferous granule reduced indirectly. Compared with the DLC film prepared without magnetic field, not only the deposition velocity of the DLC film prepared under magnetic field increased sharply, but also the mechanical hardness improved. Of the most importance, this research testified to the high efficiency of the ionization by the laser to the target, offering the base of the feasibility to the combinability between the technologies of the PLD and filtration by magnetic field.
  • [1] Xue Qunji, Wang Liping. Thin Film Materials of Carbon-base DLC[M]. Beijing:Science Press, 2012. (in Chinese)薛群基, 王立平. 类金刚石碳基薄膜材料[M]. 北京:科学出版社, 2012.
    [2] Liu Lei, Wang Tao, Huang Jinglin, et al. Diamond-like carbon thin films with high density and low internal stress deposited by coupling DC/RF magnetron sputtering[J]. Diamond Related Materials, 2016, 70(1):151-158.
    [3] Cheng Yong. Technology of Diamond-like Carbon Film Prepared by Pulsed Laser Deposition[M]. Beijing:Science Press, 2017. (in Chinese)程勇. 脉冲激光沉积类金刚石膜技术[M]. 北京:科学出版社, 2017.
    [4] Cheng Yong, Lu Yimin, Guo Yanlong, et al. Development of function films prepared by pulsed laser deposition technology[J]. Laser Optoelectronics Progress, 2015, 52(12):120003. (in Chinese)程勇, 陆益敏, 郭延龙, 等. 脉冲激光沉积功能薄膜的研究进展[J]. 激光与光电子学进展, 2015, 52(12):120003.
    [5] de Julian Fernandez C, Vassent J L, Givord D. Thin film deposition by magnetic field-assisted pulsed laser assembly[J]. Applied Surface Science, 1999, 138-139:150-154.
    [6] Hiroharu Kawasaki, Kazuya D, Satoshi Hiraishi, et al. Effects of cross-magnetic field on thin film preparation by pulsed Nd:YAG laser deposition[J]. Thin Solid Films, 2000, 374:278-281.
    [7] 戴建明, 张科军, 邹建, 等. 强磁场辅助脉冲激光沉积系统:中国, ZL201410033519[P]. 2014-05-07.
    [8] 宁廷银, 周岳亮, 赵嵩卿, 等. 一种具有可控磁场的脉冲激光沉积制膜系统:中国, ZL200610001808.7[P]. 2006-07-20.
    [9] Lu Yimin, Huang Guojun, Guo Yanlong, et al. Improved design and experiment for preparing uniform optical DLC film by large area PLD[J]. Acta Armamentarii, 2017, 38(3):555-560. (in Chinese)陆益敏, 黄国俊, 郭延龙, 等. 激光沉积大面积均匀类金刚石膜的设计改进及实验[J]. 兵工学报, 2017, 38(3):555-560.
    [10] Wan Qiang, Lu Yimin, Mi Chaowei, et al. Research on antireflective and protective diamond-like carbon film deposited by 248 nm nanosecond laser[J]. Laser Optoelectronics Progress, 2015, 52(9):093101. (in Chinese)万强, 陆益敏, 米朝伟, 等. 248nm纳秒激光沉积类金刚石增透保护膜的工艺研究[J]. 激光与光电子进展, 2015, 52(9):093101.
    [11] Neeraj Dwivedi, Sushil Kumar, Hitendra K Malik. Strange hardness characteristic of hydrogenated diamond-like carbon thin film by plasma enhanced chemical vapor deposition process[J]. Appl Phys Lett, 2013, 102:011917.
  • [1] 叶盛, 赵上熳, 邢忠福, 彭志勇, 郑宇亭, 陈良贤, 刘金龙, 李成明, 魏俊俊.  激光技术在金刚石加工中的研究及应用进展 . 红外与激光工程, 2024, 53(2): 20230567-1-20230567-22. doi: 10.3788/IRLA20230567
    [2] 张亚凯, 陈晖, 白振岙, 庞亚军, 王雨雷, 吕志伟, 白振旭.  多波长红光金刚石拉曼激光器 . 红外与激光工程, 2023, 52(8): 20230329-1-20230329-7. doi: 10.3788/IRLA20230329
    [3] 金舵, 白振旭, 范文强, 齐瑶瑶, 丁洁, 颜秉政, 王雨雷, 吕志伟.  金刚石布里渊激光器实现4倍线宽窄化 . 红外与激光工程, 2023, 52(8): 20230295-1-20230295-4. doi: 10.3788/IRLA20230295
    [4] 白振旭, 陈晖, 蔡云鹏, 丁洁, 齐瑶瑶, 颜秉政, 崔璨, 王雨雷, 吕志伟.  金刚石拉曼振荡器实现级联布里渊激光输出 . 红外与激光工程, 2022, 51(11): 20220660-1-20220660-2. doi: 10.3788/IRLA20220660
    [5] 李牧野, 杨学宗, 孙玉祥, 白振旭, 冯衍.  单频连续波金刚石拉曼激光器研究进展（特邀） . 红外与激光工程, 2022, 51(6): 20210970-1-20210970-11. doi: 10.3788/IRLA20210970
    [6] 张朝阳, 魏俊俊, 邢忠福, 彭志勇, 刘金龙, 陈良贤, 李成明.  金刚石膜表面微结构红外增透性能研究 . 红外与激光工程, 2021, 50(2): 20200199-1-20200199-8. doi: 10.3788/IRLA20200199
    [7] 白振旭, 陈晖, 张展鹏, 王坤, 丁洁, 齐瑶瑶, 颜秉政, 李森森, 闫秀生, 王雨雷, 吕志伟.  百瓦级1.2/1.5 μm双波长金刚石拉曼激光器（特邀） . 红外与激光工程, 2021, 50(12): 20210685-1-20210685-7. doi: 10.3788/IRLA20210685
    [8] 王华丰, 孙轲, 孙盛芝, 邱建荣.  飞秒激光诱导金刚石微纳结构及其应用（特邀） . 红外与激光工程, 2020, 49(12): 20201057-1-20201057-11. doi: 10.3788/IRLA20201057
    [9] 白振旭, 杨学宗, 陈晖, 金舵, 丁洁, 齐瑶瑶, 李森森, 闫秀生, 王雨雷, 吕志伟.  高功率金刚石激光技术研究进展（特邀） . 红外与激光工程, 2020, 49(12): 20201076-1-20201076-13. doi: 10.3788/IRLA20201076
    [10] 李晓静, 郑子云, 史戈平, 高永亮.  制备光学金刚石膜的微波谐振腔设计及优化 . 红外与激光工程, 2019, 48(S2): 156-163. doi: 10.3788/IRLA201948.S216001
    [11] 蒋海涛, 刘诗斌, 元倩倩.  纳米金刚石和氧化锌纳米线的协同效应提高紫外光电响应 . 红外与激光工程, 2019, 48(1): 120004-0120004(8). doi: 10.3788/IRLA201948.0120004
    [12] 陆益敏, 黄国俊, 郭延龙, 程勇, 韦尚方.  双激光制备双层结构类金刚石膜的实验研究 . 红外与激光工程, 2018, 47(11): 1121003-1121003(6). doi: 10.3788/IRLA201847.1121003
    [13] 蔡颂, 熊彪, 陈根余, 吴吉平.  青铜金刚石砂轮的激光整形与修锐 . 红外与激光工程, 2017, 46(4): 406008-0406008(10). doi: 10.3788/IRLA201746.0406008
    [14] 陆益敏, 郭延龙, 黄国俊, 黎伟, 万强, 唐璜.  脉冲激光沉积低内应力多层类金刚石膜 . 红外与激光工程, 2017, 46(9): 921001-0921001(6). doi: 10.3788/IRLA201746.0921001
    [15] 程勇, 陆益敏, 郭延龙, 黄国俊, 王淑云, 刘旭, 曹海源, 初华, 杨雪.  PLD法制备半球面均匀DLC膜的装置、仿真与实验 . 红外与激光工程, 2016, 45(6): 621004-0621004(5). doi: 10.3788/IRLA201645.0621004
    [16] 董志伟, 张伟斌, 郑立威, 姜涛, 范国祥, 赵煦, 赵清亮, 陈德应, 夏元钦.  利用飞秒激光和纳秒激光脉冲加工金刚石 . 红外与激光工程, 2015, 44(3): 893-896.
    [17] 左杨平, 卢文壮, 张圣斌, 余亚平, 冯森, 左敦稳.  面向激光防护应用的金刚石/V2O5 膜系设计与制备 . 红外与激光工程, 2015, 44(8): 2491-2495.
    [18] 凌晓, 俞树荣, 张俊彦.  沉积气压对类金刚石薄膜结构和性能的影响 . 红外与激光工程, 2014, 43(6): 1878-1882.
    [19] 于盛旺, 安康, 李晓静, 申艳艳, 宁来元, 贺志勇, 唐宾, 唐伟忠.  高功率MPCVD金刚石膜红外光学材料制备 . 红外与激光工程, 2013, 42(4): 971-974.
    [20] 付秀华, 杨永亮, 刘国军, 李琳, 潘永刚, Ewan Waddell.  大面积头罩上类金刚石薄膜均匀性研究 . 红外与激光工程, 2013, 42(1): 181-184.
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  542
  • HTML全文浏览量:  71
  • PDF下载量:  28
  • 被引次数: 0
出版历程
  • 收稿日期:  2019-07-06
  • 修回日期:  2019-08-05
  • 刊出日期:  2019-11-25

磁场辅助激光沉积类金刚石膜初探

doi: 10.3788/IRLA201948.1117002
  • 1. 陆军工程大学 光电技术研究所,湖北 武汉 430075
    • 作者简介:

    程勇(1961-),男,教授,所长,博士,主要从事激光技术及其应用方面的研究。Email:gdyjs@263.net

    通讯作者: 陆益敏(1981-),男,讲师,博士,主要从事脉冲激光沉积功能薄膜方面的研究。Email:luyimin_zy@163.com
  • 收稿日期: 2019-07-06
  • 修回日期: 2019-08-05
  • 刊出日期: 2019-11-25
基金项目:

军内科研项目（012016017000B12503）

  • 中图分类号: TN304.2

摘要: 提出了磁场辅助激光沉积类金刚石（DLC）膜技术，在硅基底附近添加磁力线向基底收拢的磁场，用以迫使侧向飞行的离子向基底靠拢并参与成膜。由于离子向基底的集中，使其在膜层中含量大幅上升，间接地减少了大颗粒的比例，因此，与无磁场条件下制备的DLC膜相比，引入磁场不仅提高了DLC膜的沉积速率，而且提高了其机械硬度；更重要的是，间接地证明了激光对靶材离化的高效性，为脉冲激光沉积（PLD）结合磁过滤技术提供了可行性的依据。

English Abstract

    全文HTML

参考文献 (11)

目录

    /

    返回文章
    返回

    版权所有 © 2019 《红外与激光工程》编辑部｜ 地址: 天津市空港经济区中环西路58号｜ 邮政编码: 300308

    津ICP备19007885号-1

    本系统由 北京仁和汇智信息技术有限公司 开发    百度统计