金属扇形层合板激光圆弧扫描变形特征研究

王焕捷,  王续跃

downloadPDF
文章导航 > 红外与激光工程  > 2019 >  48(S1): 27-34
王焕捷, 王续跃. 金属扇形层合板激光圆弧扫描变形特征研究[J]. 红外与激光工程, 2019, 48(S1): 27-34. doi: 10.3788/IRLA201948.S106005
引用本文: 王焕捷, 王续跃. 金属扇形层合板激光圆弧扫描变形特征研究[J]. 红外与激光工程, 2019, 48(S1): 27-34. doi: 10.3788/IRLA201948.S106005
shu
Wang Huanjie, Wang Xuyue. Deformation characteristics of laser circular bending in sector metal laminated plates[J]. Infrared and Laser Engineering, 2019, 48(S1): 27-34. doi: 10.3788/IRLA201948.S106005
Citation: Wang Huanjie, Wang Xuyue. Deformation characteristics of laser circular bending in sector metal laminated plates[J]. Infrared and Laser Engineering, 2019, 48(S1): 27-34. doi: 10.3788/IRLA201948.S106005
shu

金属扇形层合板激光圆弧扫描变形特征研究

doi: 10.3788/IRLA201948.S106005
  • 1.

    大连理工大学 机械工程学院 精密与特种加工教育部重点实验室,辽宁 大连 116024

基金项目: 

国家自然科学基金（51375073，51621064）

详细信息
    作者简介:

    王焕捷(1993-),男,硕士生,主要从事激光弯曲成形方面的研究。Email:751340869@qq.com

  • 中图分类号: TN249

Deformation characteristics of laser circular bending in sector metal laminated plates

  • 1.

    Key Laboratory of Precision and Non-traditional Machining Technology of the Ministry of Education,School of Mechanical Engineering,Dalian University of Technology,Dalian 116024,China

  • 摘要: 针对不锈钢-碳钢扇形层合板，采用激光同心圆弧扫描方式进行弯曲成形试验。用激光扫描仪对变形后的样件进行几何特征测量，分析激光扫描线各位置的弯曲角度及扫描线两侧曲面变形特征。研究激光加工参数和板材几何参数对扇形层合板激光圆弧扫描弯曲成形的影响。结果表明：经激光圆弧扫描后的扫描线变形区在空间呈三维曲线状，在扫描线处的弯曲角度各不相同，中线位置角度最小，并向板材左右两侧逐渐增大，于板材边缘处达到最大，关于扇形板中心线基本对称；扫描线径向两侧均产生明显曲面变形，扫描线至扇形板外圆线的区域沿y轴正向内凹，扫描线至扇形板内圆线的区域沿z轴正向外凸。研究结果为深入分析激光同心圆弧扫描三维变形机理提供试验依据。
    Abstract: For stainless steel-carbon steel sector laminated plates, the laser concentric circular scanning method was used to bend the plates. The geometrical characteristics measurement of deformed sample were measured by laser scanner. The bending angle of each position of the laser scanning lines and the deformation characteristics of the curved surface on both sides of the scanning line were analyzed. The effects of laser processing parameters and sheet geometry parameters on laser arc scanning bending of sector laminates were studied. The results show that deformation zone of the scanning line after laser circular scanning is three-dimensional curve in space and the bending angles at the scanning line are different. The angle in central line is the smallest and increases gradually to the left and right sides of the plate, reaching the maximum at the edge of the plate. The angle is basically symmetrical along the center line of the plate; The surface is obviously deformed by a curved surface and the area from the scanning line to the outer circular line of the sector plate is inwardly recessed, and the area from the scanning line to the inner circular line of the sector plate is convex outward. The research results provide a basis for in-depth understanding of the three-dimensional deformation mechanism of laser circular scanning.
  • [1] Hennige T. Development of irradiation strategies for 3D-laser forming[J]. Journal of Materials Process Technology, 2000, 103(1):102-108.
    [2] Li Zihui, Wang Xuyue. Numerical simulation of warping deformation on metal composite plate during laser bending[J]. Infrared and Laser Engineering, 2018, 47(5):0506004. (in Chinese)
    [3] Zhang Peng, Gao Hongliang, Chu Guannan. Study on laser sine forming of sheet metals[J]. Manufacturing Technology Machine Tool, 2007(3):35-38. (in Chinese)
    [4] Deng Chunfeng, Zhang Peng, Ma Yanxia. Deformation behavior of sheet metal during laser sine cosine scanning[J].China Metal Forming Equipment Manufacturing Technology, 2008, 43(5):93-95. (in Chinese)
    [5] Kant R, Bhuyan P M, Joshi S N. Experimental studies on TGM and BM dominated curvilinear laser bending of aluminum alloy sheets[C]//Lasers Based Manufacturing, 2015:69-91.
    [6] Kant R, Joshi S N. Numerical modeling and experimental validation of curvilinear laser bending of magnesium alloy sheets[J]. Proceedings of the Institution of Mechanical Engineers PART B-Journal of Engineering Manufacture, 2014, 228(9SI):1036-1047.
    [7] Kant R, Bhuyan P M, Joshi S N. Experimental studies on curvi-linear laser bending of thin sheets[C]//ICATSA 2016, 2016:539-548.
    [8] Kant R, Joshi S N. Numerical investigations into influence of scanning path curvature on deformation behavior during curvilinear laser bending of magnesium sheets[J]. Journal of Thermal Stresses, 2018, 41(3):313-330.
    [9] Nadeem Q, Seong W J, Na S J. Process designing for laser forming of circular sheet metal[J]. Chinese Optics Letters, 2012, 10(2):021405.
    [10] Nadeem Q, Na S J. An approach to form the dome shape by 3D laser forming[J]. Chinese Optics Letters, 2013, 11(2):021402.
    [11] Esfahani R T, Golabi S, Zojaji Z. Optimization of finite element model of laser forming in circular path using genetic algorithms and ANFIS[J]. Soft Computing, 2016, 20(5SI):2031-2045.
    [12] Wang Maolu, Yang Lijun. Investigation on the scanning strategy of 3D laser forming of sheet metal[J]. Journal of Plasticity Engineering, 2013(6):51-55. (in Chinese)
    [13] Ma Xupeng, Wang Xuyue, Xu Wenji, et al. Heat conduction characteristics of stainless steel-carbon steel laminated sheet bending position[J]. Laser Optoelectronics Progress, 2013, 50(10):101401. (in Chinese)
  • [1] 蒋露松, 陈宇, 海小华, 彭礼威.  激光光源汽车前照灯自由曲面反射器设计 . 红外与激光工程, 2023, 52(7): 20230321-1-20230321-10. doi: 10.3788/IRLA20230321
    [2] 叶井飞, 朱钰, 顾悠扬, 詹浣湫, 曹书琴, 魏建民, 宋真真, 曹兆楼, 郑改革.  基于正交双向迭代的自由曲面激光光束整形设计（特邀） . 红外与激光工程, 2023, 52(7): 20230299-1-20230299-10. doi: 10.3788/IRLA20230299
    [3] 李正达, 孙胜利, 孙小进, 陈异凡, 韩逸啸, 马孝浩, 申笑天.  利用神经网络反演遥感相机扫描镜热变形的方法 . 红外与激光工程, 2023, 52(10): 20230065-1-20230065-10. doi: 10.3788/IRLA20230065
    [4] 李国会, 杜应磊, 徐宏来, 向汝建, 吴晶, 谢川林, 周志强, 刘章文, 向振佼, 张秋实.  双变形镜对Yb:YAG板条激光器光束质量校正技术 . 红外与激光工程, 2022, 51(8): 20210800-1-20210800-11. doi: 10.3788/IRLA20210800
    [5] 薛亚飞, 罗子艺, 韩善果, 蔡得涛, 徐望辉, 房卫萍, 刘皓挺.  激光扫描速度对碳钢板表面锈蚀层去除质量的影响 . 红外与激光工程, 2022, 51(5): 20210389-1-20210389-5. doi: 10.3788/IRLA20210389
    [6] 张兴权, 纪看看, 王会廷, 戚晓利, 陈彬, 童靳于, 方光武.  激光冲击圆杆曲面诱导的残余应力数值模拟 . 红外与激光工程, 2019, 48(7): 706004-0706004(9). doi: 10.3788/IRLA201948.0706004
    [7] 张福才, 许文慧, 何振飞, 吕文明, 王秋, 王航宇.  相干衍射成像研究进展：叠层扫描相干衍射成像和相干调制成像 . 红外与激光工程, 2019, 48(6): 603011-0603011(13). doi: 10.3788/IRLA201948.0603011
    [8] 严惠, 王霄, 梁绘昕, 田宗军, 谢德巧, 徐国建.  选区顺序对激光直接制造TC4残余应力及变形的影响 . 红外与激光工程, 2019, 48(2): 242002-0242002(8). doi: 10.3788/IRLA201948.0242002
    [9] 王高烽, 王续跃, 王焕捷.  矩形金属层合板激光圆弧扫描弯曲曲面变形分析 . 红外与激光工程, 2019, 48(2): 242003-0242003(8). doi: 10.3788/IRLA201948.0242003
    [10] 李紫慧, 王续跃.  金属复合板激光弯曲过程中翘曲变形数值模拟 . 红外与激光工程, 2018, 47(5): 506004-0506004(7). doi: 10.3788/IRLA201847.0506004
    [11] 李紫慧, 王续跃.  层合板激光往复扫描弯曲中翘曲变形数值模拟 . 红外与激光工程, 2018, 47(12): 1206008-1206008(8). doi: 10.3788/IRLA201847.1206008
    [12] 黄志伟, 张兴权, 章艳, 裴善报, 黄志来, 陈彬.  边界约束条件对薄板激光喷丸诱导残余应力和塑性变形的影响 . 红外与激光工程, 2017, 46(8): 806009-0806009(8). doi: 10.3788/IRLA201746.0806009
    [13] 周斌, 石世宏, 邓志强, 石拓, 傅戈雁, 方琴琴.  基于中空激光光内送粉技术的扇形结构件激光成形研究 . 红外与激光工程, 2017, 46(9): 906007-0906007(6). doi: 10.3788/IRLA201746.0906007
    [14] 张耀平, 樊峻棋, 龙国云.  变形镜在激光辐照下热畸变有限元模拟 . 红外与激光工程, 2016, 45(11): 1136002-1136002(5). doi: 10.3788/IRLA201645.1136002
    [15] 李孟麟, 朱精果, 孟柘, 任建峰, 肖芳, 张珂殊.  轻小型机载激光扫描仪设计 . 红外与激光工程, 2015, 44(5): 1426-1431.
    [16] 沈晓骏, 汪诚, 安志斌, 周留成, 赖志林, 王冠.  斜激光冲击对航空发动机风扇轴弯曲疲劳性能的影响 . 红外与激光工程, 2015, 44(12): 3548-3553.
    [17] 杨光, 丁林林, 王向明, 王华明, 钦兰云.  扫描路径对激光修复钛合金残余应力与变形的影响 . 红外与激光工程, 2015, 44(10): 2926-2932.
    [18] 董繁龙, 赵方舟, 葛廷武, 王智勇.  光纤弯曲对掺镱光纤激光器光束质量的影响 . 红外与激光工程, 2014, 43(11): 3565-3569.
    [19] 孙崇利, 苏伟, 武红敢, 刘睿, 刘婷, 黄健熙, 朱德海, 张晓东, 刘峻明.  改进的多级移动曲面拟合激光雷达数据滤波方法 . 红外与激光工程, 2013, 42(2): 349-354.
    [20] 郭汝海, 陈宁, 时魁, 王兵, 施龙.  高功率激光系统中内光路热变形的仿真及实验研究 . 红外与激光工程, 2013, 42(11): 2925-2930.
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  371
  • HTML全文浏览量:  56
  • PDF下载量:  23
  • 被引次数: 0
出版历程
  • 收稿日期:  2018-11-06
  • 修回日期:  2018-12-17
  • 刊出日期:  2019-04-25

金属扇形层合板激光圆弧扫描变形特征研究

doi: 10.3788/IRLA201948.S106005
  • 1. 大连理工大学 机械工程学院 精密与特种加工教育部重点实验室,辽宁 大连 116024
    • 作者简介:

    王焕捷(1993-),男,硕士生,主要从事激光弯曲成形方面的研究。Email:751340869@qq.com

  • 收稿日期: 2018-11-06
  • 修回日期: 2018-12-17
  • 刊出日期: 2019-04-25
基金项目:

国家自然科学基金（51375073，51621064）

  • 中图分类号: TN249

摘要: 针对不锈钢-碳钢扇形层合板，采用激光同心圆弧扫描方式进行弯曲成形试验。用激光扫描仪对变形后的样件进行几何特征测量，分析激光扫描线各位置的弯曲角度及扫描线两侧曲面变形特征。研究激光加工参数和板材几何参数对扇形层合板激光圆弧扫描弯曲成形的影响。结果表明：经激光圆弧扫描后的扫描线变形区在空间呈三维曲线状，在扫描线处的弯曲角度各不相同，中线位置角度最小，并向板材左右两侧逐渐增大，于板材边缘处达到最大，关于扇形板中心线基本对称；扫描线径向两侧均产生明显曲面变形，扫描线至扇形板外圆线的区域沿y轴正向内凹，扫描线至扇形板内圆线的区域沿z轴正向外凸。研究结果为深入分析激光同心圆弧扫描三维变形机理提供试验依据。

English Abstract

    全文HTML

参考文献 (13)

目录

    /

    返回文章
    返回

    版权所有 © 2019 《红外与激光工程》编辑部｜ 地址: 天津市空港经济区中环西路58号｜ 邮政编码: 300308

    津ICP备19007885号-1

    本系统由 北京仁和汇智信息技术有限公司 开发    百度统计